Macro Perforated POF Shrink Film

Precision Perforation: Hot needle technology ensures clean, consistent holes without rough edges that could tear during high-speed wrapping
Customizable: 10cm without macro perforation on both side edges or on the open side (center folded film) ensures reliable heat sealing.
Strict Quality Control: ISO 9001 certified. Each roll inspected for thickness uniformity, hole consistency, and shrink performance
Fast Lead Time: 15-25 days for standard orders. Mixed sizes per container accepted
Sample Policy: Free samples available for quality testing (freight collect)

Material Polyolefin (LLDPE & PP)

Layer Structure: 5 Layers Co-extruded

Thickness :15, 19, 25micron

Width Customizable from 350mm to550mm

Shrinkage Ratio Up to 65% (MD & TD Balanced)

Shrink Temperature 120°C - 180°C

Finish High Gloss / Super Clear

UP-MP Macro Perforated Polyolefin Shrink Film
TEST ITEM		UNIT	ASTM TEST	TYPICAL VALUES
THICKNESS					54G	60G	68G	88G
Tensile strength (MD)		N/mm²	D882		130	130	130	125
Tensile strength (TD)		N/mm²			125	125	125	120
Elongation(MD)		%			115	115	120	120
Elongation(TD)		%			110	110	110	115
Tear (MD)		g	D1922		14.0	18.0	20.0	25.0
Tear (TD)		g	D1922		13.5	17.5	19.0	24.0
SEAL strength(MD)		N/mm	F88		1.20	1.30	1.30	1.50
SEAL strength(TD) /HOT WIRE SEAL		N/mm	F88		1.35	1.40	1.40	1.65
COF Dynamic (Film to film)			D1894		0.22	0.21	0.18	0.19
COF Static			D1894		0.22	0.21	0.18	0.19
Haze			D1003		2.40	2.40	2.60	2.90
Clarity			D1746		98.5	98.5	98.0	98.0
Gloss @ 45deg			D2457		90.0	89.0	89.0	88.0
Oxygen Transmission Rate		cc/m³/day	D3985		10210.0	9700.0	8700.0	7600.0
Water Vaper Transmission Rate		gm/m³/day	F1249		38.0	33.0	26.0	22.0
Free Shrinkage				MD			TD
	100℃	%	D2732		19.00		28.00
	110℃				38.00		45.00
	120℃				70.00		72.00
	130℃				81.00		79.00
Shrink Tension		Mpa	D2838	MD			TD
	100℃				2.20		2.70
	110℃				2.70		3.60
	120℃				2.80		3.80
	130℃				3.00		4.10
Storage conditions required : Below 30 degrees Celsius, no direct sunlight.
Maximum storage time: 12 months.